(Basicity) on pellet physical, metallurgical and microstructural properties basic studies have been carried out on hematite iron ore fines with limestone addition from 0 to 780% in the green mix to obtain pellet basicity (CaO/SiO 2) 008 to 115 2 Pelletization Process at JSW Steel Limited Production of iron oxide pellets from iron ore
2021年9月20日 It is, therefore, essential to acquire detailed knowledge of the formation principle of liquid phase in highsilica iron ores pellets with varying CaO/SiO 2 ratios and MgO contents Umadevi et al investigated the influence of basicity (CaO/SiO 2) from 0 to 11 on the properties and microstructure of iron ore pellets The pellet properties were
2021年2月20日 Iron ore pellet physicochemical properties are known to be derived by its basicity Thus, in the present work, an investigation is presented on the effect of basicity on the industrial pellet properties PC Mahapatra, M Ranjan, Influence of pellet basicity (CaO/SiO2) on iron ore pellet properties and microstructure ISIJ Int 51(1), 14
2022年10月2日 The results show that by only adopting traditional magnetization roasting–magnetic separation, an iron ore concentrate containing 5749% Fe and 14% P 2 O 5 at an iron recovery rate of 875% and a dephosphorization rate of 3427% was produced, indicating that it is difficult to effectively dephosphorize and upgrade iron by
2019年9月10日 And a correlation between reduction rate and applied load was obtained which greatly depended on the basicity of iron oxide pellets Xu et al demonstrated that the addition of dolomite was favorable for the reduction swelling property of iron ore pellets RSI of pellets decreased from 133 to 40 vol% as the content of dolomite increased from
2014年1月10日 To better guide the industrial production, the effect of binary basicity (CaO/SiO 2) on the reduction swelling behavior and mechanism of limestone fluxed iron ore pellets was investigated Meanwhile, Xray diffraction technique was used to analyze the phase transformation in pellets with different basicity during the reduction process, and
2021年11月1日 The iron and steel metallurgy industry faces the question of how to replace carbon in iron ore reduction to reduce CO 2 emission in basic industries and achieve the expectation of "double carbon" This study investigates the reduction swelling of individual iron ore pellet under mixed H 2CO atmospheres and at temperatures of 800–1000 ℃ by
2022年10月2日 The development of blast furnace smelting technology with a high proportion of pellets is an important means for improving the utilization rate of complex coassociated mineral resources The effect of basicity on the reduction swelling performance of pellets prepared from Bayan Obo iron ore concentrate is characterized by the aspects of
2021年7月15日 The reduction behaviour of high flux hardened iron ore pellets of basicity 2, 4, 6 and 8 (Basicity = CaO/SiO 2) reduced at temperature (900–1050 °C) were examined and reported hereThe kinetic model [(1 − α) (−1/3) − 1] 2 = kt was found to be the best fit model with the present experimental data Activation energy was calculated based on the
2021年1月1日 The present study concentrates on investigation of the possibilities of making high basicity reduced iron ore pellets (DRI) at low cost, which can be further used in the pig iron refining or steel making technology in EAF/LD Converter process The reduction behaviour of high flux (basicity 2, 4, 6 8) hardened iron ore pellets, reduced at
2022年1月1日 The iron and steel metallurgy industry faces the question of how to replace carbon in iron ore reduction to reduce CO 2 emission in basic industries and achieve the expectation of "double carbon" This study investigates the reduction swelling of individual iron ore pellet under mixed H 2CO atmospheres and at temperatures of 800–1000 ℃ by
2021年11月1日 The volume expansion caused by crystal structure transformation during the reduction from hematite (αFe 2 O 3) to maghemite (γFe 2 O 3) was the fundamental reason for the swelling of
The influence mechanism of basicity on the reduction swelling index (RSI) of iron ore briquettes was investigated using the SEM analysis and Factsage 73 thermodynamic calculations based on the addition of pure CaO to
2015年8月10日 The iron and steel metallurgy industry faces the question of how to replace carbon in iron ore reduction to reduce CO 2 emission in basic industries and achieve the expectation of "double carbon" This study investigates the reduction swelling of individual iron ore pellet under mixed H 2CO atmospheres and at temperatures of 800–1000 ℃ by
2023年4月27日 The reduction behaviour of high flux hardened iron ore pellets of basicity 2, 4, 6 and 8 (Basicity = CaO/SiO2) reduced at temperature (900–1050 °C) were examined and reported here
2011年5月8日 The effect of pellet basicity and MgO content on the melt formation and microstructure during the induration of iron ore pellets was examined Fired pellets with varying basicity (0 to 08) and MgO (0 and 15%) content were tested for cold strength, reduction degradation index, reducibility, swelling and softening–melting characteristics
2021年2月1日 With the rise of pellets basicity from 002 to 040, the higher compressive strength of fired pellets and the shorter roasting time were achieved The maximum RSI decreased from 23% to 17% during hydrogenrich reduction, while the compressive strength increased from 500 to 1070 N/pellet Iron ore pellets are produced in the range from
2021年4月12日 The effects of SiO2 content on the preparation process and metallurgical properties of acid oxidized pellets, including compressive strength, reduction, and softening—melting behaviors, were systematically investigated Mineralogical structures, elemental distribution, and pore size distribution were varied to analyze the mechanism
2022年6月20日 The application of fluxed pellets in iron making industry has attracted considerable attention because of the better metallurgical properties than acid pellets and environmental friendliness compared to sinters However, fluxed pellets with different binary basicity (CaO/SiO2) exhibited significant differences in phase composition,
2021年6月22日 The influence mechanism of basicity on the reduction swelling index (RSI) of iron ore briquettes was investigated using the SEM analysis and Factsage 73 thermodynamic calculations based on the